Performance and stability analysis of SOFC containing thin and dense gadolinium-doped ceria interlayer sintered at low temperature

Yige Wang, Chuan Jia, Zewei Lyu, Minfang Han, Junwei Wu, Zaihong Sun, Fumitada Iguchi, Keiji Yashiro, Tatsuya Kawada

研究成果: Article査読

抄録

Gadolinium-doped ceria (GDC) interlayers are required to prevent the interfacial reaction between La0.6Sr0.4Co0.2Fe0.8O3 (LSCF) cathode and Y2O3-stabilized ZrO2 (YSZ) electrolyte in solid oxide fuel cells (SOFCs). However, it's difficult to prepare a thin and dense GDC interlayer on the sintered half-cell at a low temperature. In this study, the physical vapor deposition (PVD) method was employed to successfully manufacture dense GDC interlayers with the thickness of 1 μm. The influences of GDC sintering temperature (900 °C, 1000 °C and 1100 °C) on cell performance characteristics and degradation behavior were investigated. The cell with GDC interlayer sintered at 1100 °C showed the lowest degradation rate during the 216-h operation. The best stability was attributed to the most effective inhibition of Sr diffusion by the GDC interlayer, which was demonstrated by the almost unchanged Ohmic and polarization resistances during the aging stage and the negligible Sr enrichment at YSZ/GDC interface. Compared to the conventional screen-printed GDC interlayers (sintered above 1250 °C), the GDC interlayer prepared by the PVD method and sintered at 1100 °C was significantly denser and thinner, showing a promising application prospect due to its benefits for cell stability.

本文言語English
ジャーナルJournal of Materiomics
DOI
出版ステータスAccepted/In press - 2021

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 表面、皮膜および薄膜
  • 金属および合金

フィンガープリント

「Performance and stability analysis of SOFC containing thin and dense gadolinium-doped ceria interlayer sintered at low temperature」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル