Oxygen nonstoichiometry of the perovskite-type oxide La 1-xCaxCrO3-δ (x=0.1, 0.2, 0.3)

Shigenori Onuma, Keiji Yashiro, Shogo Miyoshi, Atsushi Kaimai, Hiroshige Matsumoto, Yutaka Nigara, Tatsuya Kawada, Junichiro Mizusaki, Kenichi Kawamura, Natsuko Sakai, Harumi Yokokawa

研究成果: Article査読

54 被引用数 (Scopus)

抄録

The oxygen nonstoichiometry, δ, of La1-xCa xCrO3-δ (x=0.1-0.3) was measured by means of thermogravimetry as a function of oxygen partial pressure, P(O2), temperature, T, between 1073 and 1373 K, and the content of calcium, x. In any compositions, δ becomes larger and is getting closer to δ=x/2 with decreasing P(O2). At the same P(O2), δ of La 1-xCaxCiO3-δ increases with increasing T and x. There is almost no difference in oxygen nonstoichiometry between Ca-doped lanthanum chromite and Sr-doped lanthanum chromite. Defect chemical analysis was performed taking defect interaction into consideration. The nonstoichiometry curves were reproduced well by the proposed defect model and the obtained thermodynamic parameters. The influence of defect interaction on defect formation energy can be mainly attributed to change in interatomic potential due to defect-induced lattice expansion.

本文言語English
ページ(範囲)287-293
ページ数7
ジャーナルSolid State Ionics
174
1-4
DOI
出版ステータスPublished - 2004 10月 29

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Oxygen nonstoichiometry of the perovskite-type oxide La 1-xCaxCrO3-δ (x=0.1, 0.2, 0.3)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル