Oxidation and hardness profile of V-Ti-Cr-Si-Al-Y alloys

Mitsuhiro Fujiwara, Manabu Satou, Akira Hasegawa, Katsunori Abe

研究成果: Article査読

9 被引用数 (Scopus)

抄録

Several alloys of composition V^Ti-4Cr-(0-0.5)Si-(0-0.5)Al-(0-0.5)Y were selected for oxidation in air. In addition a V-4Ti-4Cr-0.5Si-0.5Al-0.5Y alloy was pre-implanted with helium to study the effect of helium on oxidation behavior. Rapid oxidation experiments in air were conducted on tensile specimens and disc bend specimens at 300°C, 500°C, 600°C and 700°C for 1 h. After oxidation, tensile specimens were mounted in cross-section, and micro-indentation hardness tests were conducted. The depths of increased hardness obtained by indentation tests and the thickness of cleavage fracture zones measured by using scanning electron microscopy (SEM) micrographs were similar. The hardness profile of the cross-section in the depth direction corresponded to a model of oxygen diffusion in vanadium. Three-point bend tests were conducted on helium-implanted and air- exposed disc specimens. The bending stress of the specimen with 700 appm helium was larger than that with 70 appm helium.

本文言語English
ページ(範囲)1311-1315
ページ数5
ジャーナルJournal of Nuclear Materials
283-287
PART II
DOI
出版ステータスPublished - 2000

ASJC Scopus subject areas

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

フィンガープリント 「Oxidation and hardness profile of V-Ti-Cr-Si-Al-Y alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル