Optical and scintillation properties of LuGd2Al2Ga3O12:Ce, Lu2GdAl2Ga3O12:Ce, and Lu2YAl2Ga3O12:Ce single crystals: A comparative study

Warut Chewpraditkul, Nakarin Pattanaboonmee, Weeeapong Chewpraditkul, Tomasz Szczesniak, Marek Moszynski, Kei Kamada, Akira Yoshikawa, Romana Kucerkova, Martin Nikl

研究成果: Article査読

抄録

Optical and scintillation properties of LuGd2Al2Ga3O12:Ce, Lu2GdAl2Ga3O12:Ce, and Lu2YAl2Ga3O12:Ce single crystals are compared. The blue-shift of 5d1→ 4f photoluminescence emission (PL) band is observed upon partial substitution of Gd3+ with a smaller Lu3+ (or Y3+) ion. At 662 keV γ-rays, the light yield of 35,400 ± 1,700 ph/MeV obtained for LuGd2Al2Ga3O12:Ce is higher than that of 29,200 ± 1,500 ph/MeV and 20,200 ± 1,000 ph/MeV for Lu2GdAl2Ga3O12:Ce and Lu2YAl2Ga3O12:Ce, respectively. Scintillation decays are approximated by sum of exponentials with the fast component decay time and relative intensity of 78 ns (42%) for LuGd2Al2Ga3O12:Ce, 48 ns (71%) for Lu2GdAl2Ga3O12:Ce and 45 ns (88%) for Lu2YAl2Ga3O12:Ce, which leads to a superior coincidence time resolution of Lu2YAl2Ga3O12:Ce. PL decay time at 110 K and 290 K, afterglow characteristics, and mass attenuation coefficient at 59.5 keV and 662 keV γ - rays are also presented.

ASJC Scopus subject areas

  • 核物理学および高エネルギー物理学
  • 器械工学

フィンガープリント

「Optical and scintillation properties of LuGd<sub>2</sub>Al<sub>2</sub>Ga<sub>3</sub>O<sub>12</sub>:Ce, Lu<sub>2</sub>GdAl<sub>2</sub>Ga<sub>3</sub>O<sub>12</sub>:Ce, and Lu<sub>2</sub>YAl<sub>2</sub>Ga<sub>3</sub>O<sub>12</sub>:Ce single crystals: A comparative study」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル