Nucleation and growth behavior of undercooled Pd42.5Cu30Ni7.5P20 melt

Nobuyuki Nishiyama, Akihisa Inoue

研究成果: Article査読

5 被引用数 (Scopus)


An undercooled Pd42.5Cu30Ni7.5P20 melt with a eutectic composition exhibits the lowest critical cooling rate for glass formation of 0.067 K/s. Nucleation and crystal growth behaviors of the undercooled melt were investigated at 683 K where the temperature is close to nose temperature. Nucleation frequency and crystal growth rate were evaluated as 4.77 × 109/m3·s and 3.24 × 10-7 m/s, respectively. These values are almost the same as those for the undercooled Pd40Cu30Ni10P20 melt which has a slightly off-eutectic composition. However, the difference in incubation time for crystallization and nucleation mode was observed in both melts. Based on these results, the compositional effect on the stability of undercooled melt is discussed in the present study.

ジャーナルMaterials Transactions
出版ステータスPublished - 2002 5

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Nucleation and growth behavior of undercooled Pd<sub>42.5</sub>Cu<sub>30</sub>Ni<sub>7.5</sub>P<sub>20</sub> melt」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。