NiZnCu ferrite thick film with nano scale crystallites formed by the aerosol deposition method

Maxim Lebedev, Jun Akedo, Atsushi Iwata, Satoshi Sugimoto, Kouichiro Inomata

研究成果: Article査読

18 被引用数 (Scopus)

抄録

This paper describes the magnetic properties of NiZnCu ferrite film deposited at room temperature by an aerosol deposition method (ADM). The thickness of the film was 6 μm and the deposition rate was estimated as 2 μm/min. The microstructure of as-deposited at room temperature films consists of randomly oriented nanocrystallites with a size of 20 nm. As-deposited and annealed films exhibited the following magnetic properties: intensity of magnetization Ms = 0.147 T (117 emu/cm3), coercivity Hc = 40.58 kA/m (510 Oe); and Ms = 0.3 T (250 emu/cm3), Hc = 14.95 kA/m (188 Oe), respectively.

本文言語English
ページ(範囲)1621-1624
ページ数4
ジャーナルJournal of the American Ceramic Society
87
9
DOI
出版ステータスPublished - 2004 9

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 材料化学

フィンガープリント

「NiZnCu ferrite thick film with nano scale crystallites formed by the aerosol deposition method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル