Morphology and domain pattern of L10 ordered FePt films

G. Q. Li, H. Takahoshi, H. Ito, H. Saito, S. Ishio, T. Shima, K. Takanashi

研究成果: Article査読

57 被引用数 (Scopus)

抄録

Magnetic force microscope (MFM) was used to characterize the L1 0 ordered FePt(001) films sputter deposited on MgO(001) substrates. It was found that the morphology varied from isolated particles to continuous films when the nominal thickness (tN) was changed. The coercivity showed a marked change at the percolation boundary of tN ≅ 45 nm.