Microstructure of pressureless-sintered Al2O3-24 vol% ZrO2 composite studied by high-resolution electron microscopy

B. T. Lee, K. Hiraga, Daisuke Shindo, A. Nishiyama

研究成果: Article査読

15 被引用数 (Scopus)

抄録

The microstructure of an Al2O3-24 vol% ZrO2 composite prepared by pressureless-sintering was investigated by high-resolution electron microscopy. The composite was formed of homogeneously dispersed ZrO2 and Al2O3 grains with average sizes of 0.3 and 0.5 μm, respectively. Most ZrO2 grains had a monoclinic structure, but a few ZrO2 embedded in Al2O3 grains were a tetragonal structure. At interfaces between ZrO2 with a lamella-type twin structure and Al2O3, microcracks were observed, in addition to strain fields in the Al2O3 matrix. Complex twin structures accompanied by dislocations were observed in ZrO2 with a spherical shape. In in situ observations with electron-beam heating, it was found that a crack propagated along an Al2O3/ZrO2 interface and stopped at the place where a tetragonal ZrO2 had undergone a structural change to monoclinic ZrO2.

本文言語English
ページ(範囲)959-964
ページ数6
ジャーナルJournal of Materials Science
29
4
DOI
出版ステータスPublished - 1994 1 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Microstructure of pressureless-sintered Al<sub>2</sub>O<sub>3</sub>-24 vol% ZrO<sub>2</sub> composite studied by high-resolution electron microscopy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル