Microstructure and mechanical properties of Mg-Al-Ca-Nd alloys fabricated by gravity casting and extrusion process

Hyeon Taek Son, Jae Seol Lee, Ik Hyun Oh, Dae Guen Kim, Kyosuke Yoshimi, Kouichi Maruyama

研究成果: Article査読

11 被引用数 (Scopus)

抄録

The as-cast microstructure of Mg-5Al-3Ca-xNd alloys consists of equiaxed a-Mg matrix, (Mg, Al)2Ca eutectic phase and Al-Nd rich intermetallic compounds. With the increase of Nd addition, a-Mg matrix morphology was changed from dendritic to equiaxed grains due to suppression of grain growth by formation of homogeneous intermetallic compounds containing Nd dispersed at grain boundary and a-Mg matrix. And the grain size of as-cast alloys was decreased as addition of Nd was increased. This eutectic phase of the extruded alloys was elongated to extrusion direction and size of this phase was redined comparing to that of as-cast alloys because of severe deformation during hot extrusion. Maximum yield and ultimate tensile strength value of the as-extruded alloys was 322 and 335 MPa at Mg-5Al-3Ca-2Nd alloy, respectively.

本文言語English
ページ(範囲)1025-1031
ページ数7
ジャーナルMaterials Transactions
49
5
DOI
出版ステータスPublished - 2008 5

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Microstructure and mechanical properties of Mg-Al-Ca-Nd alloys fabricated by gravity casting and extrusion process」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル