Microstructure and mechanical properties of Al2 O3/Y3Al5O12/ZrO2 ternary eutectic materials

J. H. Lee, A. Yoshikawa, Y. Murayama, Y. Waku, S. Hanada, T. Fukuda

研究成果: Article

37 被引用数 (Scopus)

抄録

Directionally solidified fibers and rods have been grown from the ternary Al2O3/Y3Al5O12 /ZrO2 system using micro-pulling-down method. Fiber diameter could be varied 0.3 mm-2 mm at pull-rates ranging 6-900 mm/h and 500 mm in length. The ternary eutectic fibers had homogeneous colony patterned eutectic microstructures. The interlamellar spacing λ exhibited an inverse-square-root dependence on the growth speed v according to λ = 8 × v-1/2, where λ has the dimension of μm and v is in μm/s. The tensile strength was recorded 1730 MPa at 25 °C and 1100 MPa at 1200 °C for a fiber crystals grown at a growth speed of 900 mm/h. Eutectic rods having 5 mm of diameter and up to 80 mm in length were also successfully grown by the micro-pulling-down method. The eutectic rods showed 1400 MPa of mechanical strength by compressive mode at 1500 °C with homogeneous colony microstructures.

本文言語English
ページ(範囲)1411-1417
ページ数7
ジャーナルJournal of the European Ceramic Society
25
8 SPEC. ISS.
DOI
出版ステータスPublished - 2005

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント 「Microstructure and mechanical properties of Al<sub>2</sub> O<sub>3</sub>/Y<sub>3</sub>Al<sub>5</sub>O<sub>12</sub>/ZrO<sub>2</sub> ternary eutectic materials」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル