Microstructure and Magnetic Properties of the Aerosol-Deposited Sm-Fe-N Thick Films

Tomohito Maki, Satoshi Sugimoto, Toshio Kagotani, Koichiro Inomata, Jun Akedo

研究成果: Article査読

抄録

In this study, the relationship among magnetic properties, Aerosol Deposition (AD) conditions and microstructures in Sm-Fe-N AD films were investigated. The maximum thickness of 145 μm was obtained in the AD conditions of gas flow rate (gfr) = 6 L/min for 10 min. The density of Sm-Fe-N films were in the range of 5.43-6.24 g/cm3, which were 71-81 % of the X-ray density of the Sm2Fe17N3 compound reported (7.67 g/cm3). The Sm-Fe-N AD films showed remanence in the range of 0.38-0.42 T, which were 61-68 % of that of Sm-Fe-N host powder (0.62 T). The coercivities increased from 1.16 to 1.74-1.79 T after the deposition because the grain size decreased from 1.94 to 0.32 μm.

本文言語English
ページ(範囲)887-891
ページ数5
ジャーナルIEEJ Transactions on Fundamentals and Materials
124
10
DOI
出版ステータスPublished - 2004

ASJC Scopus subject areas

  • Electrical and Electronic Engineering

フィンガープリント 「Microstructure and Magnetic Properties of the Aerosol-Deposited Sm-Fe-N Thick Films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル