Microstructure and electrical conductivity of SrRuO3 thin films prepared by laser ablation

Akihiko Ito, Hiroshi Masumoto, Takashi Goto

研究成果: Article査読

25 被引用数 (Scopus)

抄録

SrRuO3 (SRO) thin films were prepared by laser ablation, and the effects of deposition conditions on the microstructure and electrical conductivity of these films were investigated by changing the substrate temperature (Tsub) and deposition atmosphere. The SRO thin films deposited on quartz substrates in a high vacuum (P = 10-6 Pa) and an oxygen partial pressure (PO2) of 0.13 Pa were amorphous, independent of Tsub. Pseudo-cubic SRO thin films were obtained at PO2 = 13 Pa and Tsub > 773 K. The Sr to Ru ratio increased with increasing Tsub, and free Ru was contained in SRO films prepared at P = 10-6 Pa. The crystal grain coarsened with increasing T sub and PO2. The electrical conductivity (σ) of SRO thin films increased with increasing Tsub and PO2, and the highest σ was obtained at Tsub = 973 K and PO2 = 13 Pa. The σ of SRO films mainly changed with the Sr/Ru ratio and the surface morphology. The change of σ associated with the magnetic phase transition was observed at 163 K.

本文言語English
ページ(範囲)2808-2814
ページ数7
ジャーナルMaterials Transactions
47
11
DOI
出版ステータスPublished - 2006 11

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Microstructure and electrical conductivity of SrRuO<sub>3</sub> thin films prepared by laser ablation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル