Microstructure and densification of ZrB2-SiC composites prepared by spark plasma sintering

Ipek Akin, Mikinori Hotta, Filiz Cinar Sahin, Onuralp Yucel, Gultekin Goller, Takashi Goto

研究成果: Article査読

91 被引用数 (Scopus)

抄録

ZrB2-SiC composites were prepared by spark plasma sintering (SPS) at temperatures of 1800-2100 °C for 180-300 s under a pressure of 20 MPa and at higher temperatures of above 2100 °C without a holding time under 10 MPa. Densification, microstructure and mechanical properties of ZrB2-SiC composites were investigated. Fully dense ZrB2-SiC composites containing 20-60 mass% SiC with a relative density of more than 99% were obtained at 2000 and 2100 °C for 180 s. Below 2120 °C, microstructures consisted of equiaxed ZrB2 grains with a size of 2-5 μm and α-SiC grains with a size of 2-4 μm. Morphological change from equiaxed to elongated α-SiC grains was observed at higher temperatures. Vickers hardness of ZrB2-SiC composites increased with increasing sintering temperature and SiC content up to 60 mass%, and ZrB2-SiC composite containing 60 mass% SiC sintered at 2100 °C for 180 s had the highest value of 26.8 GPa. The highest fracture toughness was observed for ZrB2-SiC composites containing 50 mass% SiC independent of sintering temperatures.

本文言語English
ページ(範囲)2379-2385
ページ数7
ジャーナルJournal of the European Ceramic Society
29
11
DOI
出版ステータスPublished - 2009 8 1

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント 「Microstructure and densification of ZrB<sub>2</sub>-SiC composites prepared by spark plasma sintering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル