Zn-11%Al-3%Mg-0.2%Si めっき鋼板の切断端面における防食機構

Yuki Suzuki, Shinichi Yamaguchi, Masamitsu Matsumoto, Izumi Muto

研究成果: Article査読

抄録

Zinc and zinc alloy coated steel is widely utilized for home appliance, construction, automobile, and so on for its high corrosion resistance. In this work, corrosion behavior at cut edges of Zn-11%Al-3%Mg-0.2%Si alloy coated steel sheets (SD) was investigated with cyclic wet-dry corrosion test. The result showed that SD have the superior anti-corrosive property to zinc coated steel sheets (GI) at early period of corrosion. GI produced red rust, whereas SD produced no red rust. After the cyclic wet-dry corrosion test, zinc-containing white rust deposited on steel substrate. In the case of SD, magnesium reached the center of cut edge and larger area on the steel was covered with white rust. With polarization measurements of steel substrate on which white rust deposited, it was clarified that white rust of SD reduced both anodic and cathodic current density of steel substrate more largely than that of GI. In the case of SD, galvanic current between steel substrate with white rust and coating layer was small compared with GI. It was suggested this anti-corrosive property of SD is due to magnesium-containing white rust.

寄稿の翻訳タイトルMechanism of corrosion protection at cut edge of Zn-11%Al-3%Mg-0.2%Si coated steel sheets
本文言語Japanese
ページ(範囲)752-758
ページ数7
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
105
7
DOI
出版ステータスPublished - 2019

Keywords

  • Corrosion product
  • Cut edge
  • Electrochemical property
  • Zinc coated steel
  • Zn-11%Al-3%Mg-0.2%Si

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Zn-11%Al-3%Mg-0.2%Si めっき鋼板の切断端面における防食機構」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル