Mechanically activated synthesis of single crystalline MgO nanostructures

M. Nusheh, H. Yoozbashizadeh, M. Askari, H. Kobatake, H. Fukuyama

研究成果: Article査読

12 被引用数 (Scopus)

抄録

One-dimensional (1D) MgO structures were successfully synthesized via carbothermic reduction of mechanically activated mixture of MgO and graphite. Mechanical activation of source materials before carbothermic reduction can substantially enhance the formation of MgO products at a temperature (1000 °C) relatively lower than that required in previous approaches (≥1200 °C). However, the morphology of MgO formed is dependent on the degree of mechanical activation and the condition of the subsequent carbothermic reduction. Two distinctive morphologies were found for MgO products synthesized using our method: single crystalline nanorods with rectangular cross-sections whose diameters range from 50 to 100 nm, and microfibers (∼5 μm in diameter) with and without branching. The synthesized products were systematically studied by XRD, SEM, TEM, and EDS. The results show that the nucleation and growth process of these morphologies seem to be a vapor-solid mechanism.

本文言語English
ページ(範囲)715-720
ページ数6
ジャーナルJournal of Alloys and Compounds
506
2
DOI
出版ステータスPublished - 2010 9 17

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Mechanically activated synthesis of single crystalline MgO nanostructures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル