Maskless selective growth of semi-polar (1 12̄ 2) GaN on Si (3 1 1) substrate by metal organic vapor phase epitaxy

Min Yang, Hyung Soo Ahn, Tomoyuki Tanikawa, Yoshio Honda, Masahito Yamaguchi, Nobuhiko Sawaki

研究成果: Article査読

13 被引用数 (Scopus)

抄録

Semi-polar (1 1 2̄ 2) GaN layers were selectively grown by metal organic chemical vapor phase epitaxy on patterned Si (3 1 1) substrates without SiO2 amorphous mask. The (1 1 2̄ 2) GaN layers could be selectively grown only on Si (1 1 1) facets when the stripe mask width was narrower than 1 μm even without SiO2. Inhomogeneous spatial distribution of donor bound exciton (DBE) peak in low-temperature cathodoluminescence (CL) spectra was explained by the difference of growth mode before and after the coalescence of stripes. It was found that the emission intensity related crystal defects is drastically decreased in case of selective growth without SiO2 masks as compared to that obtained with SiO2 masks.

本文言語English
ページ(範囲)2914-2918
ページ数5
ジャーナルJournal of Crystal Growth
311
10
DOI
出版ステータスPublished - 2009 5 1

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

フィンガープリント 「Maskless selective growth of semi-polar (1 12̄ 2) GaN on Si (3 1 1) substrate by metal organic vapor phase epitaxy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル