Low-temperature synthesis of Sr1-xCaxCuO2 from hydroxide precursor

Masatsune Kato, Ichiro Nagai, Yoji Koike

研究成果: Article査読

4 被引用数 (Scopus)

抄録

The alkaline-earth copper oxides Sr1-xCaxCuO2 (0 ≤ x ≤ 1) have been synthesized in flowing gas of N2 or O2 by thermal decomposition of hydroxide precursors Sr1-xCaxCu(OH)4 · H2O. In the first step, we have succeeded in obtaining hydroxide precursors Sr1-xCaxCu(OH)4 · H2O with 0 ≤ x ≤ 1 in the form of a precipitation in a highly concentrated NaOH solution. In the second step, namely, in the process of thermal decomposition, the hydroxide precursors have been found to be decomposed into an amorphous condition at a temperature as low as 200°C. The ambient-pressure phase of SrCuO2 is obtained by heating the hydroxide precursors for 12 h at 500°C and 700°C in flowing gas of N2 and O2, respectively. The reaction temperature is much lower than the 1000°C in flowing gas of O2 in the conventional solid-state reaction method. With increasing x up to 0.7, the temperature at which the ambient-pressure phase of Sr1-xCaxCuO2 appears increases in flowing gas of both N2 and O2. The so-called infinite-layer compound of Sr1-xCaxCuO2 is obtained in a narrow range of x around 0.9 at ∼ 1000°C in flowing gas of O2, which is similar to the result in the conventional solid-state reaction method. For x ∼ 1, the ambient-pressure phase of Ca1-xCuO2 (y ∼ 0.15) appears in the temperature range between 600°C and 800°C only in flowing gas of O2.

本文言語English
ページ(範囲)275-281
ページ数7
ジャーナルSolid State Ionics
108
1-4
DOI
出版ステータスPublished - 1998 5月 1

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Low-temperature synthesis of Sr1-xCaxCuO2 from hydroxide precursor」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル