Leaching rate of hematite in hydrochloric acid solutions in agitated vessel

Katsutoshi Matsumoto, Shoji Taniguchi, Atsushi Kikuchi

研究成果: Article査読

抄録

A kinetic study on the leaching of Fe2O3 in HCl solutions has been made by using agitated vessel to clarify the mechanism of the rate acceleration which was found in the previous study for Fe2O3-HNO3 system. Powder specimens with various sizes were prepared by a wet classification of ground powder obtained from pellets sintered at 1623 K (I) and 1523 K (II). The specific areas of these specimens were measured before and after the leaching experiments. Leaching rates were found to be independent of the agitation speed. Leaching rates under various conditions were correlated by the following relationship: r = 20.0(1+5.4α1.6) Sw0 exp (-94000/RT)CH(+)CCl(-), where α is the fraction dissolved, Sw0 the initial specific area of the specimen, T temperature, C concentration of ionic species. As seen in the above correlation, the leaching rate increased with increasing α. In order to clarify the mechanism of the rate acceleration, a leaching experiment was carried out by using a sintered Fe2O3 disk of which surface was polished and exposed to a HCl solution. Same as the previous study, only the (0001) oriented crystal planes were found to dissolve and its dissolution rate increased with time. The fractional area of the (0001) plane was about 25%. Assuming the same fractional area for the powder specimen, the increase in the overall surface area was well estimated.

本文言語English
ページ(範囲)297-302
ページ数6
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
58
3
DOI
出版ステータスPublished - 1994

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Leaching rate of hematite in hydrochloric acid solutions in agitated vessel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル