Joining characteristics of orthodontic wires with laser welding

Masahiro Iijima, William A. Brantley, Toshihiro Yuasa, Takeshi Muguruma, Isao Kawashima, Itaru Mizoguchi

研究成果: Article査読

18 被引用数 (Scopus)

抄録

Laser welding 0.016 × 0.022 in. β-Ti, Ni-Ti, and Co-Cr-Ni orthodontic wires was investigated by measuring joint tensile strength, measuring laser penetration depth, determining metallurgical phases using micro X-ray diffraction (micro-XRD), and examining microstructures with an scanning electron microscope (SEM). Welding was performed from 150 to 230 V. Mean tensile strength for Ni-Ti groups was significantly lower (p < 0.05) than for most other groups of laser-welded specimens. Although mean tensile strength for β-Ti and Co-Cr-Ni was significantly lower than for control specimens joined by silver soldering, it was sufficient for clinical use. The β-Ti orthodontic wire showed deeper penetration depth from laser welding than the Ni-Ti and Co-Cr-Ni orthodontic wires. Micro-XRD patterns of laser-welded β-Ti and Ni-Ti obtained 2 mm from the boundary were similar to as-received specimens, indicating that original microstructures were maintained. When output voltages of 190 V and higher were used, most peaks from joint areas disappeared or were much weaker, perhaps because of a directional solidification effect, evidenced by SEM observation of fine striations in welded β-Ti. Laser welding β-Ti and Co-Cr-Ni wires may be acceptable clinically, since joints had sufficient strength and metallurgical phases in the original wires were not greatly altered.

本文言語English
ページ(範囲)147-153
ページ数7
ジャーナルJournal of Biomedical Materials Research - Part B Applied Biomaterials
84
1
DOI
出版ステータスPublished - 2008 1 1
外部発表はい

ASJC Scopus subject areas

  • 生体材料
  • 生体医工学

フィンガープリント

「Joining characteristics of orthodontic wires with laser welding」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル