Irradiation-induced microstructural evolution and swelling of 3C-SiC

Yan Ru Lin, Ching Shun Ku, Chun Yu Ho, Wei Tsung Chuang, Sosuke Kondo, Ji Jung Kai

研究成果: Article査読

13 被引用数 (Scopus)

抄録

In this study, an ion-irradiated single crystal 3C-SiC under fluences of up to 20 dpa at 400-1350 °C was examined using synchrotron based X-ray diffraction and high resolution transmission electron microscopy. Interstitial clusters, dislocation loops, Frank loops, stacking fault loops, and voids in 3C-SiC were investigated. The high resolution TEM results show that clusters collapsed to {1 1 1} small loops when their size reached few nm with increasing temperature, and gradually develop into Frank loops with an added atomic layer along {1 1 1} at 1000 °C. Interplanar spacing information of single crystal SiC was obtained from synchrotron XRD radial scan measurements. Irradiation-induced volume swelling at 400-1350 °C was measured, and the anisotropic (a = b < c) swelling behavior of SiC was confirmed. In addition, humps on the right side of SiC (0 0 2) were observed, which suggested that C+/Si+-Si〈1 0 0〉 and/or C+/Si+-C〈1 0 0〉 dumbbells gave rise to diffuse scattering.

本文言語English
ページ(範囲)276-283
ページ数8
ジャーナルJournal of Nuclear Materials
459
DOI
出版ステータスPublished - 2015 4
外部発表はい

ASJC Scopus subject areas

  • 核物理学および高エネルギー物理学
  • 材料科学(全般)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「Irradiation-induced microstructural evolution and swelling of 3C-SiC」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル