Influence of SiO2 and Fe2O3 on properties and microstructure of β″-alumina

Yasuhiko Tsuru, Yoshimi Yashima, Akihiro Sawata, Yuichiro Murakami, Yuichi Ikuhara

    研究成果: Article査読

    1 被引用数 (Scopus)

    抄録

    In order to decrease the cost of β-alumina for solid electrolytes of AMTEC (alkali metal thermo-electric converter), it is desirable to use low purity starting materials. In this paper, we investigated the influence of impurities such as SiO2 and Fe2O3, which are usually contained in low purity alumina, for several hundreds ppm, on properties and microstructure of β″-alumina. The content of β″-alumina phase and the density decreased with the addition of SiO2, and the resistivity of β″-alumina increased even with the addition of amounts of SiO2 as small as 500 ppm. Additional SiO2 formed as a glassy phase at multiple grain junctions, but no secondary phase was observed at boundaries between two adjacent grains. Si segregated along the grain boundaries. It was suggested that the segregated Si suppressed the sintering and increased the resistivity. The addition of Fe 2O3 did not affect the properties such as content of β″-alumina phase, density and resistance, but the addition of Fe 2O3 in ≥0.5 mass% resulted in grain growth. Because Fe ions were suggested dissolved in spinel block of β″-alumina, it was considered that Fe2O3 did not influence the properties of β″;-alumina.

    本文言語English
    ページ(範囲)102-107
    ページ数6
    ジャーナルJournal of the Ceramic Society of Japan
    110
    1278
    DOI
    出版ステータスPublished - 2002 2

    ASJC Scopus subject areas

    • セラミックおよび複合材料
    • 化学 (全般)
    • 凝縮系物理学
    • 材料化学

    フィンガープリント

    「Influence of SiO<sub>2</sub> and Fe<sub>2</sub>O<sub>3</sub> on properties and microstructure of β″-alumina」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル