Influence of Al content on martensitic transformation behavior in Zr 50Cu 50-xAl x

F. Q. Meng, K. Tsuchiya, F. X. Yin, S. Ii, Yoshihiko Yokoyama

研究成果: Article査読

22 被引用数 (Scopus)

抄録

Influence of Al content on martensitic transformation temperature in ZrCu phase was investigated by differential scanning calorimetry for a series of Zr 50Cu 50-xAl x alloys. The crystallographic structure of the martensite was predominantly a monoclinic Cm, which is a superstructure of B19′. Microstructural observations revealed that a higher Al content above 6 mol% led to a pronounced formation of Zr 2Cu and τ 5 phases forming complex eutectic microstructures. The electron probe microanalysis indicated that the Al atoms in ZrCu phase substitute the Cu atoms up to 6 mol% and the excess Al atoms exist mainly in the τ 5 phase. The increasing Al content from 0 to 6 mol% induced a decrease in the martensitic transformation start temperature, M s, from 446 K to 311 K, and in the reverse martensitic transformation start temperature, A s, from 537 K to 468 K. But M s remained almost constant when the Al content is over 6 mol%. Thus, the substitution of the Cu atoms by the Al atoms in ZrCu phase led to the decrease in M s and A s.

本文言語English
ページ(範囲)136-140
ページ数5
ジャーナルJournal of Alloys and Compounds
522
DOI
出版ステータスPublished - 2012 5 5

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Influence of Al content on martensitic transformation behavior in Zr <sub>50</sub>Cu <sub>50-x</sub>Al <sub>x</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル