In vitro aging test for bioactive PMMA-based bone cement using simulated body fluid

S. B. Cho, S. B. Kim, K. J. Cho, I. Y. Kim, C. Ohtsuki, M. Kamitakahara

研究成果: Article査読

7 被引用数 (Scopus)

抄録

Novel PMMA-based bone cement using bioactivc sol-gel derived CaO-SiO 2 powder in order to induce bioactivity as well as to increase its mechanical property. The novel PMMA-based bone cements formed apatite on their surfaces in Simulated Body Fluid(SBF). In the present study, a change in mechanical property of the cement was evaluated using SBF. Before soaking in SBF, its compressive strength showed 80.6±2.1MPa. After soaking in SBF for 2 weeks, Sweeks and 9 weeks, its compressive strength were changed to 83.6±1.6MPa, 87.3±2.4MPa and 85.6±1.8MPa, respectively. It is clear that from the above result, there is no decrease in its compressive strength within 9 weeks soaking in SBF. That it hardly decreases in compressive strength of 7P3S bone cement in SBF is due to the relative small amount of gel powder or its spherical shape and monosize. Therefore, the newly developed PMMA-based cement can bond to the living bone and also be effectively used as bioactive bone cement without decrease in mechanical property.

本文言語English
ページ(範囲)153-156
ページ数4
ジャーナルKey Engineering Materials
284-286
DOI
出版ステータスPublished - 2005
外部発表はい

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「In vitro aging test for bioactive PMMA-based bone cement using simulated body fluid」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル