Improvement of the piezoelectric properties of PVDF-HFP using AgNWs

Liangke Wu, Guiwen Huang, Ning Hu, Shaoyun Fu, Jianhui Qiu, Zhongchang Wang, Ji Ying, Zichen Chen, Weiguo Li, Shan Tang

    研究成果: Article査読

    38 被引用数 (Scopus)


    In order to improve the piezoelectric properties of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP), we added various amounts of silver nanowires (AgNWs) into PVDF-HFP and N,N-dimethylformamide (DMF) solution to prepare composite films. Stretching and poling were applied to the films to induce the formation of the polar β-phase and reorientation of the dipole moment. The crystal structure of the films was investigated by polarized optical microscopy (POM), Fourier transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC). The obtained results showed that the phase transformation mainly occurred in stretching and the reorientation of the dipole moment was attributed to poling. It was also concluded that the AgNWs played a role as nucleate agents in the β-phase formation and the phase transformation. The piezoelectric properties were also evaluated by the output voltage and harvested power density. It was found that the open circuit voltage of 0.1 wt% AgNWs containing films was 52% higher than that of pure PVDF-HFP films. Furthermore, the harvested power density was increased by 159%. Overdose of AgNWs resulted in crystal defects and the lower degree of crystallinity, leading to worse piezoelectric properties. This journal is

    ジャーナルRSC Advances
    出版ステータスPublished - 2014

    ASJC Scopus subject areas

    • 化学工学(全般)
    • 化学 (全般)


    「Improvement of the piezoelectric properties of PVDF-HFP using AgNWs」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。