Improvement of soft magnetic properties by simultaneous addition of P and Cu for nanocrystalline FeNbB alloys

Akihiro Makino, Masaki Bingo, Teruo Bitoh, Kunio Yubuta, Akihisa Inoue

研究成果: Article査読

23 被引用数 (Scopus)

抄録

The additional effect of P and/or Cu on the structure and the magnetic properties of Fe-Nb-B nanocrystalline soft magnetic alloy tapes with a wide width of 5 mm produced in air was investigated. Although Cu or P addition changes the magnetic softness a little, only the simultaneous addition of 1 at. % P and 0.1 at. % Cu significantly improves the soft magnetic properties of the crystallized alloys. The best magnetic properties (higher permeability than 45× 103, lower coercivity than 5 Am, and saturation magnetic flux density of 1.50-1.54 T) were obtained in the compositional ranges of 6.6-6.8 at. % Nb and 8.4-8.8 at. % B with 1% P and 0.1% Cu, and these values are superior to the typical nanocrystallized Fe84 Nb7 B9 alloy prepared in a vacuum. The improvement probably originates from the decrease in the distribution of the α-Fe grain size in the crystallized structure by the simultaneous addition.

本文言語English
論文番号09N117
ジャーナルJournal of Applied Physics
101
9
DOI
出版ステータスPublished - 2007 5 21

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント 「Improvement of soft magnetic properties by simultaneous addition of P and Cu for nanocrystalline FeNbB alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル