Improvement of Jc for GdBCO coated conductors by annealing under strain

Takumi Suzuki, Satoshi Awaji, Hidetoshi Oguro, Kazuo Watanabe, Michinaka Sugano, Shutaro MacHiya, Masugu Sato, Teruo Izumi, Yuh Shiohara

研究成果: Article査読

2 被引用数 (Scopus)

抄録

GdBa2Cu3Oy coated conductors were annealed under external strain (strain-annealing). The residual strain after annealing was evaluated using synchrotron radiation. We found that the residual strain is changed by the strain-annealing. The volume fraction of the a-axis domains along the longitudinal direction is increased by compression-annealing and decreased by tension-annealing. In addition, the Jc value of the tension-annealed sample increases drastically below 70 K, although the J c value is smaller than that of the as-received sample at 77.3 K for B. The peak of the angular dependent Jc at θ = 0°, which originates from the c-axis correlated pinning, for the strain-annealed sample is much smaller than that of the as-received sample. It is considered that the shrinking of the c-axis correlated pinning because of the reduction of the twin structure and the increase of carrier doping may be related to the change in Jc properties.

本文言語English
論文番号6359783
ジャーナルIEEE Transactions on Applied Superconductivity
23
3
DOI
出版ステータスPublished - 2013 1 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

フィンガープリント 「Improvement of J<sub>c</sub> for GdBCO coated conductors by annealing under strain」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル