Impact property of low-activation vanadium alloy after laser welding and heavy neutron irradiation

Takuya Nagasaka, Takeo Muroga, Hideo Watanabe, Takeshi Miyazawa, Masanori Yamazaki, Kenji Shinozaki

研究成果: Article

7 引用 (Scopus)

抜粋

Weld specimens of the reference low activation vanadium alloy, NIFS-HEAT-2, were irradiated up to a neutron fluence of 1.5 × 1025 n m -2 (E > 0.1 MeV) (1.2 dpa) at 670 K and 1.3 × 10 26 n m-2 (5.3 dpa) at 720 K in the JOYO reactor in Japan. The base metal exhibited superior irradiation resistance with the ductile-to-brittle transition temperature (DBTT) much lower than room temperature (RT) for both irradiation conditions. The weld metal kept the DBTT below RT after the 1.2 dpa irradiation; however, it showed enhanced irradiation embrittlement with much higher DBTT than RT after the 5.3 dpa irradiation. The high DBTT for the weld metal was effectively recovered by a post-irradiation annealing at 873 K for 1 h. Mechanisms of the irradiation embrittlement and its recovery are discussed, based on characterization of the radiation defects and irradiation-induced precipitation.

元の言語English
ページ(範囲)S364-S369
ジャーナルJournal of Nuclear Materials
442
発行部数1-3 SUPPL.1
DOI
出版物ステータスPublished - 2013

ASJC Scopus subject areas

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

フィンガープリント Impact property of low-activation vanadium alloy after laser welding and heavy neutron irradiation' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用