Hydrogen embrittlement of high strength steels and environmental hydrogen entry

Eiji Akiyama, Songjie Li, Zuogui Zhang, Maoqiu Wang, Katsuhiro Matsukado, Kaneaki Tsuzaki, Boping Zhang

研究成果: Conference contribution

9 被引用数 (Scopus)

抄録

Delayed fracture properties of martensitic high strength steels have been evaluated by measuring the change in fracture stress of circumferentially notched bar specimens pre-charged with hydrogen by means of slow strain rate test (SSRT). The fracture stress of a steel with higher strength level showed sharper decrease indicating higher susceptibility to delayed fracture. It has been found that the decrease of fracture stress with hydrogen concentration follows a power law relationship when intergranular fracture mode is observed. Another finding is that the local stress and the local hydrogen concentration estimated by finite element analysis are determining delayed fracture. Hydrogen entry into steels caused by atmospheric corrosion has been evaluated as well by using cyclic corrosion test (CCT) simulating atmospheric corrosion. The circumferentially notched bar specimens were exposed to the CCT condition and SSRT was performed at humid environment to investigate both hydrogen entry and its influence on the decrease of fracture stress in the environment. The relation between fracture stress and the content of hydrogen in corrosive environment was compared with the relation of hydrogen pre-charged specimens. The SSRT combined with CCT was proposed as evaluation method considering both the effect of hydrogen in metals and hydrogen entry into metals.

本文言語English
ホスト出版物のタイトルProceedings of the 2008 International Hydrogen Conference - Effects of Hydrogen on Materials
ページ54-61
ページ数8
出版ステータスPublished - 2009 12月 1
外部発表はい
イベント2008 International Hydrogen Conference - Effects of Hydrogen on Materials - Jackson, WY, United States
継続期間: 2008 9月 72008 9月 10

出版物シリーズ

名前Proceedings of the 2008 International Hydrogen Conference - Effects of Hydrogen on Materials

Other

Other2008 International Hydrogen Conference - Effects of Hydrogen on Materials
国/地域United States
CityJackson, WY
Period08/9/708/9/10

ASJC Scopus subject areas

  • 材料化学
  • 核物理学および高エネルギー物理学
  • 原子分子物理学および光学

フィンガープリント

「Hydrogen embrittlement of high strength steels and environmental hydrogen entry」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル