純 Ni および Ni–Cr 合金における水素脆化挙動の結晶粒径依存性

Naohiro Kobayashi, Motomichi Koyama, Kenji Kobayashi, Tomohiko Hojo, Eiji Akiyama

研究成果: Article査読

1 被引用数 (Scopus)

抄録

The grain size effects on the hydrogen embrittlement susceptibility of pure Ni and Ni–20Cr alloy were investigated. The hydrogen embrittlement susceptibility was evaluated by tensile testing under electrochemical hydrogen charging. Relative elongation, defined as the elongation under hydrogen charging divided by elongation in air, increased with increasing grain size in pure Ni (the grain size was in the range of 11–22 µm). In contrast, the relative elongation of Ni–20Cr alloy increased with decreasing grain size from 13 to 1.8 µm. Correspondingly, intergranular fracture was suppressed by grain coarsening in pure Ni and grain refinement in the Ni–20Cr alloy. In addition, the intergranular fracture surface in pure Ni showed curved slip lines, and in the Ni–20Cr alloy showed straight line marks. These fractographic features imply that the mechanisms of the hydrogen–assisted intergranular crack growth were different in pure Ni and Ni–20Cr alloy and this can be attributed to the difference in stacking fault energy.

寄稿の翻訳タイトルHydrogen embrittlement behavior of pure ni and ni–20cr alloy with different grain sizes
本文言語Japanese
ページ(範囲)49-58
ページ数10
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
85
2
DOI
出版ステータスPublished - 2021

Keywords

  • Fracrography
  • Grain refinement
  • Hydrogen embrittlement
  • Intergranular fracture
  • Nickel alloy

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「純 Ni および Ni–Cr 合金における水素脆化挙動の結晶粒径依存性」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル