HRTEM observation of alpha-phase in Al added 60/40 Cu-Zn alloy

Akihiro Maeda, Kenji Matsuda, Junya Nakamura, Tokimasa Kawabata, Susumu Ikeno, Yasuhiro Uetani

研究成果: Conference contribution

抄録

The effect of Al-addition on the mechanism of phase decomposition from β1 to α-phase in Cu-40at.%Zn alloy (base alloy) has been investigated using hardness measurement and HRTEM observation. The peak hardness during annealing and the number density of α-phase in Al-bearing alloy were the same as those in the base alloy. Many striations which have been considered as the periodicity of 9R structure were observed in the α-phase of the Al-bearing alloy. There were a lot of striations in the α-phase at the early annealing time, and the number of these striations decreased with increasing annealing time. The rate of decreasing of this striation in the α-phase of the Al-bearing alloy was the slower than that of the base alloy. According to the analysis of the selected area electron diffraction (SAED) patterns obtained for these α-phase in those alloys, transition time from the 9R structure to fcc structure t(9R-fcc) of has been detected by the changing of angles in SAED patterns. The t(9R-fcc) of α-phase in the Al-bearing alloy showed the slower than the base alloy.

本文言語English
ホスト出版物のタイトルTHERMEC 2011 Supplement
ページ586-589
ページ数4
DOI
出版ステータスPublished - 2012
イベント7th International Conference on Processing and Manufacturing of Advanced Materials, THERMEC'2011 - Quebec City, QC, Canada
継続期間: 2011 8 12011 8 5

出版物シリーズ

名前Advanced Materials Research
409
ISSN(印刷版)1022-6680

Other

Other7th International Conference on Processing and Manufacturing of Advanced Materials, THERMEC'2011
国/地域Canada
CityQuebec City, QC
Period11/8/111/8/5

ASJC Scopus subject areas

  • 工学(全般)

フィンガープリント

「HRTEM observation of alpha-phase in Al added 60/40 Cu-Zn alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル