HREM Observation of the Interface between Laves-phases and Matrix Phases in Inconel 718 by Using a High-voltage Electron Microscope

Masayuki Segawa, Akira Taniyama, Daisuke Shindo

研究成果: Article査読

抄録

The Ni-base alloy, Inconel 718 was observed with high-resolution electron microscopy using by a high-voltage electron microscope in order to analyze the morphology of the interface between Laves-phases and the austenite matrix phases. The Laves-phase had a plate shape and had a (004)Laves∥ {111}γ; [11̄0]Laves∥ <110>γ relationship in the interface with the matrix (γ). The interface had the step-structure although the interface looked like a planar shape macroscopically. It was considered that the step-structures were introduced to relax the lattice strain between the Laves-phases and the matrix. The step-structures were observed at intervals of almost 11.4-40.4 nm and 2.3-9.6 nm in the samples aged at 1 073 and 1 123 K, respectively. It was considered that the decrease of the interval of step-structure was due to the increase of the lattice strain between the Laves-phases and the matrix with increasing the aging temperature from 1 073 to 1 123 K.

本文言語English
ページ(範囲)1375-1378
ページ数4
ジャーナルIsij International
38
12
DOI
出版ステータスPublished - 1998
外部発表はい

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「HREM Observation of the Interface between Laves-phases and Matrix Phases in Inconel 718 by Using a High-voltage Electron Microscope」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル