Highly thermostable high molecular-weight low k PIM polymers based on 5,5′,6,6′-tetrahydroxy-3,3,3′,3′-Tetramethylspirobisindane, decafluorobiphenyl, and bisphenols

Yu Konno, Ryota Osuga, Junko N. Kondo, Rongbin Ye, Tadashi Tsukamoto, Yoshiyuki Oishi, Yuji Shibasaki

研究成果: Article査読

抄録

High-molecular-weight (number average molecular weight Mn = 11–81 kDa) polymers with intrinsic microporosity (PIM) were prepared by the solution polycondensation of 5,5′,6,6′-tetrahydroxy-3,3,3′,3′-tetramethyl-1,1′-spirobisindane, decafluorobiphenyl, and bisphenols in an aprotic polar solvent at an initial monomer concentration of 0.1 mol/L at 100°C-140 °C for 10–144 h. Transparent (minimum cutoff wavelength of 310 nm), highly thermostable (glass transition temperature of 161°C-376 °C by dynamic mechanical analysis, and 5% weight loss temperature in N2 of 410°C-514 °C) polymer films were fabricated using a solvent-cast method. The copolymer films showed good mechanical properties (tensile strengths of 45–67 MPa, breaking elongation of 2.2%–23.1%, and tensile elastic moduli of 1.5–3.3 GPa) and insulating properties (relative permittivity of 2.27–2.59, and dissipation factor of 0.00191–0.00466 at 20 GHz frequency). The prepared new PIM copolymers are candidates for next-generation low k dielectric materials.

本文言語English
論文番号124072
ジャーナルPolymer
230
DOI
出版ステータスPublished - 2021 9 16
外部発表はい

ASJC Scopus subject areas

  • 有機化学
  • ポリマーおよびプラスチック
  • 材料化学

フィンガープリント

「Highly thermostable high molecular-weight low k PIM polymers based on 5,5′,6,6′-tetrahydroxy-3,3,3′,3′-Tetramethylspirobisindane, decafluorobiphenyl, and bisphenols」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル