High tensile strength fiber of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] processed by two-step drawing with intermediate annealing

Taizo Kabe, Chizuru Hongo, Toshihisa Tanaka, Takaaki Hikima, Masaki Takata, Tadahisa Iwata

研究成果: Article

9 引用 (Scopus)

抜粋

High tensile strength fibers of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] [P(3HB-co-3HH)], a type of microbial polyesters, were processed by one-step and two-step cold-drawn method with intermediate annealing. Thermal degradation behaviors were characterized by differential scanning calorimeter and gel permeation chromatography measurements. Thermal analyses were revealed that molecular weights decreased drastically within melting time at a few minute. One-step cold-drawn fiber with drawing ratio of 10 showed tensile strength of 281 MPa, while tensile strength of as-spun fiber was 78 MPa. When two-step drawing was applied for P(3HB-co-3HH) fibers, the tensile strength was led to 420 MPa. Furthermore, the optimization of intermediate annealing condition leads to enhance the tensile strength at 552 MPa of P(3HB-co-3HH) fiber. Wide-angel X-ray diffraction measurements of these fibers suggest that the fibers with high tensile strength include much amount of the planer-zigzag conformation (β-form) as molecular conformation together with 21helix conformation (α-form).

元の言語English
記事番号41258
ジャーナルJournal of Applied Polymer Science
132
発行部数2
DOI
出版物ステータスPublished - 2015 1 1

ASJC Scopus subject areas

  • Chemistry(all)
  • Surfaces, Coatings and Films
  • Polymers and Plastics
  • Materials Chemistry

フィンガープリント High tensile strength fiber of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] processed by two-step drawing with intermediate annealing' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用