High-temperature stability of ThMn12 magnet materials

Kurima Kobayashi, Daiki Furusawa, Shunji Suzuki, Tomoko Kuno, Kimiko Urushibata, Noritsugu Sakuma, Masao Yano, Tetsuya Shoji, Akira Kato, Akira Manabe, Satoshi Sugimoto

研究成果: Article査読

10 被引用数 (Scopus)

抄録

The nitrogenated alloys (Nd0.7Zr0.3)(Fe0.75Co0.25)11.5Ti0.5N1.3 (A) and Nd(Fe0.8Co0.2)11Mo1.0N1.0 (B) and the non-nitrogenated alloy (Sm0.8Zr0.2)(Fe0.75Co0.25)11.5Ti0.5 (C), having a ThMn12 structure, show interesting magnetic properties and are candidate materials for high-temperature magnets. In this study, the stability of these materials was studied using Curie temperature measurements, differential scanning calorimetry, differential thermal analysis, thermogravimetry from room temperature to 1573 K, and X-ray diffraction of treated samples. The nitrogenated samples (A) and (B) started to decompose into the ¡-(Fe, Co) phase and other X-ray amorphous phases from about 800 and 1000 K, respectively. Sample (C) exists as a metastable phase at room temperature and decomposed above 700 K at a relatively high oxygen partial pressure (PO2 > 10 Pa), but the ThMn12 structure remained up to at least 1373 K in an almost oxygen-free atmosphere (PO2 < 10115 Pa). Sample (C) is intrinsically stable at temperatures higher than about 1000 K up to the melting temperature, which was estimated to be 1480 K. The ThMn12 structure in both R = Nd and Sm starting alloys is metastable at room temperature, and becomes unstable under 8001000 K. The decomposition rate was clearly dependent on the PO2 in the heated atmosphere, as high PO2 led to sample oxidation, and on the sample composition.

本文言語English
ページ(範囲)1845-1853
ページ数9
ジャーナルMaterials Transactions
59
11
DOI
出版ステータスPublished - 2018 1 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「High-temperature stability of ThMn<sub>12</sub> magnet materials」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル