High temperature protonic conduction in LaBO3 with the aragonite-type structure

Koji Amezawa, Nobuyuki Takahashi, Naoto Kitamura, Yoichi Tomii, Naoichi Yamamoto

研究成果: Conference article査読

15 被引用数 (Scopus)

抄録

Electrical conduction in lanthanum orthoborates LaBO3 with the orthorhombic aragonite-type structure (S. G.: Pnam) was investigated by using conductivity measurements under 0.4-5 kPa of p(H2O) and 0.01-100 kPa of p(O2) at 500-930°C. From humidity dependence and H/D isotope effect of the conductivity, it was found that LaBO3 exhibited dominantly protonic conduction under wet conditions by substituting Sr for La. Results of conductivity measurements under various p (H2O) and p(O2) suggested that the contribution of electron hole conduction became significant as temperature increased, p(O2) increased and p(H2O) decreased, although protonic conduction was estimated as predominant under the conditions used. The conductivities of the 1 mol% Sr-doped LaBO3 were 1 × 10-5 -2 × 10 -4 S cm-1 under moisturized conditions at 500-930°C. The conductivity behaviors as well as the conductivity values of the Sr-doped LaBO3 with the aragonite-type structure were quite similar to those of the acceptor-doped rare earth orthophosphates, indicating a similar proton conduction mechanism in these oxoacid salts.

本文言語English
ページ(範囲)575-579
ページ数5
ジャーナルSolid State Ionics
175
1-4
DOI
出版ステータスPublished - 2004 11 30
外部発表はい
イベントFourteenth International Conference on Solid State Ionics - Monterey, CA., United States
継続期間: 2003 6 222003 6 27

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「High temperature protonic conduction in LaBO<sub>3</sub> with the aragonite-type structure」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル