High-temperature oxidation behavior of PbTe and oxidation-resistive glass coating

Lidong Chen, Takashi Goto, Rong Tu, Toshio Hirai

研究成果: Paper査読

5 被引用数 (Scopus)

抄録

Oxidation of lead telluride (PbTe) is a serious issue for the thermoelectric application. In the present study, the oxidation behavior of PbTe was studied at oxygen partial pressures of 10 Pa to 0.1 MPa in the temperature range between 700 and 900 K. At moderately low oxygen partial pressures and high temperatures, mass loss was observed and the oxide layers (Pb3TeO5 or Pb5TeO7) formed on the PbTe surface. At high oxygen partial pressures and low temperatures, mass gain was observed and PbTeO3 or Pb2TeO4/PbTeO3 oxide layers formed on the PbTe surface. When the temperature was higher than 819 K, PbTeO3 melted and dropped down from the specimen. Oxidation-resistive glasses were coated on the PbTe surface. The glass-coated PbTe showed excellent oxidation resistance showing no mass change at 773 K.

本文言語English
ページ[d]251-254
出版ステータスPublished - 1997 12 1
イベントProceedings of the 1997 16th International Conference on Thermoelectrics, ICT'97 - Dresden, Ger
継続期間: 1997 8 261997 8 29

Other

OtherProceedings of the 1997 16th International Conference on Thermoelectrics, ICT'97
CityDresden, Ger
Period97/8/2697/8/29

ASJC Scopus subject areas

  • 工学(全般)

フィンガープリント

「High-temperature oxidation behavior of PbTe and oxidation-resistive glass coating」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル