High-temperature mechanical behavior of B2 type IrAl doped with Ni

A. Chiba, T. Ono, X. G. Li, S. Takahashi

研究成果: Conference article査読

抄録

Constant-velocity and constant-load compression tests have been conducted to examine the mechanical behavior of polycrystalline IrAl and Ir1-xNixAl at ambient and elevated temperatures. Although IrAl exhibits brittle fracture before or immediately after yielding below 1073K, steady-state deformation takes place at temperatures higher than 1273K. Ductility of Ir1-xNixAl is improved with increasing x. On the contrary, strength decreases with increasing x. IrAl exhibits the 0.2% flow stress of 1200MPa at 1073K and 350MPa at 1473K, about an order of magnitude higher than NiAl. Secondary creep of IrAl and Ir0.2Ni0.8Al(i.e., modified NiAl) exhibits class II and class I behavior respectively. Creep strength of binary IrAl and modified NiAl with Ir is about a magnitude of 4 higher than that of single-phase and multi-phase NiAl at a given applied stress.

本文言語English
ページ(範囲)707-712
ページ数6
ジャーナルMaterials Research Society Symposium - Proceedings
460
出版ステータスPublished - 1997 1 1
外部発表はい
イベントProceedings of the 1996 MRS Fall Meeting - Boston, MA, USA
継続期間: 1996 12 21996 12 6

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「High-temperature mechanical behavior of B2 type IrAl doped with Ni」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル