High-pressure synthesis of hydrides in Ca-Mg-Ni systems

H. Takamura, H. Kakuta, Y. Goto, Atsunori Kamegawa, M. Okada

研究成果: Article

22 引用 (Scopus)

抜粋

The high-pressure synthesis of new hydrides of the Ca-Mg-Ni system and crystal structural and thermal analyses have been conducted. The high-pressure synthesis was carried out at 1073 K for 2h at 5 GPa using a cubic-anvil-type apparatus. An additional hydrogen source was used to stabilize the hydride phases. A series of (Ca1-xMgx)2NiHδ was found to form solid solutions in the range of x = 0-0.4. The crystal structure of the (Ca1-xMgx)2NiHδ solid solutions was of the CsCl-type. The lattice constant of the CsCl-type phase decreased from 0.35542(2) nm (x = 0) to 0.35478(2) nm (x = 0.4) with increasing Mg content. For the samples with a Ni-rich composition, in addition to the CsCl-type phase, a Mg2Ni3H3.4 phase was also present at high pressures. The CsCl-type phases were thermally stable less than 646 ±2 K, regardless of Mg content.

元の言語English
ページ(範囲)1301-1304
ページ数4
ジャーナルMaterials Transactions
42
発行部数7
DOI
出版物ステータスPublished - 2001 1 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント High-pressure synthesis of hydrides in Ca-Mg-Ni systems' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用