High-pressure sintering behavior of α″-Fe16N 2 nanopowder

Kenta Takagi, Misaho Akada, Kimihiro Ozaki, Naoya Kobayashi, Tomoyuki Ogawa, Yasunobu Ogata, Migaku Takahashi

研究成果: Article査読

23 被引用数 (Scopus)

抄録

α″-Fe16N2 nanopowder was sintered at high-pressure and low temperature in order to explore its feasibility as a bulk magnet. TEM observation confirmed that the nanopowder was densely consolidated by sintering at a pressure of 1.2 GPa and temperatures around 200 C. Increasing the sintering temperature enhanced the densification, leading to a suppression of oxidization. However, XRD analysis revealed that sintering at 222 C caused the decomposition α″ → α-Fe + ε-Fe3N, which reduced the saturated magnetization (Ms) and coercivity (H c). Consequently, sintering at 190 C produced a dense magnet that retained the Ms of the raw powder due to the avoidances of oxidization and decomposition. On the other hand, it was found that H c degrades after sintering, which is believed to be due to magnetic interaction between the particles.

本文言語English
論文番号103905
ジャーナルJournal of Applied Physics
115
10
DOI
出版ステータスPublished - 2014 3 14

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「High-pressure sintering behavior of α″-Fe<sub>16</sub>N <sub>2</sub> nanopowder」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル