Toetsu Shishido, Kunio Kudou, Shigeru Okada, Y. E. Jinhua, Akira Yoshikawa, Kazuo Obara, Takamasa Sugawara, Hiroyuki Horiuchi, Tsuguo Fukuda

研究成果: Article査読

抄録

Polycrystals of ErRh3Bx: are synthesized by arc melting. The compounds of ErRh3Bx have a perovskite-type cubic structure (space group: Pm3̄m). The nonstoichiometric phase exists for the boron content from x= 1.000 (20 mol% B) to 0.61 (13.3 mol% B). The lattice parameter of a depends on x, and varies linearly from a = 0.4151 nm (x= 1.000) to 0.4063 nm (x=0.61). The micro-Vickers hardness of the ErRh3Bx compaunds increases with increasing their B content. The hardness of ErRh3B1.000 (20 mol% B) sample is 8.6±0.3 GPa. The thermo gravimetric curve indicates that the onset-temperature of oxidation for ErRh3B1.000 is 1303 K. The weight gain of ErRh3B1.000 during heating in air to 1473 K is 0.7%.

本文言語English
ページ(範囲)1011-1015
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
108
11
DOI
出版ステータスPublished - 2000

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 化学 (全般)
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Hardness and oxidation resistance of nonstoichiometric ErRh<sub>3</sub>B<sub>x</sub>-perovskite」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル