Growth of epitaxial orthorhombic YO1.5-substituted HfO2 thin film

Takao Shimizu, Kiliha Katayama, Takanori Kiguchi, Akihiro Akama, Toyohiko J. Konno, Hiroshi Funakubo

研究成果: Article査読

82 被引用数 (Scopus)

抄録

YO1.5-substituted HfO2 thin films with various substitution amounts were grown on (100) YSZ substrates by the pulsed laser deposition method directly from the vapor phase. The epitaxial growth of film with different YO1.5 amounts was confirmed by the X-ray diffraction method. Wide-area reciprocal lattice mapping measurements were performed to clarify the crystal symmetry of films. The formed phases changed from low-symmetry monoclinic baddeleyite to high-symmetry tetragonal/cubic fluorite phases through an orthorhombic phase as the YO1.5 amount increased from 0 to 0.15. The additional annular bright-field scanning transmission electron microscopy indicates that the orthorhombic phase has polar structure. This means that the direct growth by vapor is of polar orthorhombic HfO2-based film. Moreover, high-temperature X-ray diffraction measurements showed that the film with a YO1.5 amount of 0.07 with orthorhombic structure at room temperature only exhibited a structural phase transition to tetragonal phase above 450°C. This temperature is much higher than the reported maximum temperature of 200°C to obtain ferroelectricity as well as the expected temperature for real device application. The growth of epitaxial orthorhombic HfO2-based film helps clarify the nature of ferroelectricity in HfO2-based films (186 words/200 words).

本文言語English
論文番号032910
ジャーナルApplied Physics Letters
107
3
DOI
出版ステータスPublished - 2015 7 20

ASJC Scopus subject areas

  • 物理学および天文学(その他)

フィンガープリント

「Growth of epitaxial orthorhombic YO<sub>1.5</sub>-substituted HfO<sub>2</sub> thin film」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル