Growth of {100}-faceted NaFeTiO4 crystals with a tunable aspect ratio from a NaCl-Na2SO4 binary flux

Tomohito Sudare, Daiki Kawaura, Kunio Yubuta, Fumitaka Hayashi, Katsuya Teshima

研究成果: Article査読

7 被引用数 (Scopus)


The controlled growth of needle-shaped and planar bar-shaped NaFeTiO4 crystals, a CaFe2O4-type structure, was carried out by a flux method using a NaCl-Na2SO4 binary flux. NaCl fluxes have been empirically investigated for growing unique anisotropic crystal shapes. However, strategies for controlling the crystal morphology based on NaCl fluxes have not been established. In this study, Na2SO4 was added to a NaCl flux to supply O2- ions, which is essential for the dissolving ability of a metal oxide into ions, and the growth manner was systematically investigated as a function of flux composition. As a result, needle-shaped crystals were obtained from the pure NaCl flux with exposed {100} facets. Meanwhile, with the binary flux, the morphology of the crystals changed from a needle shape to a planar bar shape depending on the Na2SO4 content, where the aspect ratio of the {100} facets was increased by about ten times. It was found out that the aspect ratio of the {100} planes of NaFeTiO4 crystals can be controlled kinetically by the cooperative effect of Na+ ions and anionic species in the flux; Na+ ions stabilize the {100} facets and a high O2-/Cl- ratio increases the concentration of ions as a precursor for crystal growth to promote the growth in the <001> direction, resulting in planar bar-shaped crystals. We believe that the morphological control regime demonstrated here in the growth of NaFeTiO4 crystals in a NaCl-Na2SO4 binary flux could be a useful idea in high temperature chemistry and for their desirable applications.

出版ステータスPublished - 2018

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学


「Growth of {100}-faceted NaFeTiO4 crystals with a tunable aspect ratio from a NaCl-Na2SO4 binary flux」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。