Growth model and the effect of CuO nanocrystallites on the properties of chemically derived epitaxial thin films of YBa 2Cu 3O 7-x

Takeshi Araki, Toshiharu Niwa, Yutaka Yamada, Izumi Hirabayashi, Junko Shibata, Yuichi Ikuhara, Kazumi Kato, Takeharu Kato, Tsukasa Hirayama

    研究成果: Article査読

    34 被引用数 (Scopus)

    抄録

    In metalorganic deposition using trifluoroacetates (TFA-MOD), CuO nanocrystallites in calcined film, which influence the critical current density (J c) of the resulting film, have seldom been considered before. CuO nanocrystallites ripen and grow during the calcining process at 200-250°C and grow into large CuO grains in the YBa 2Cu 3O 7-x (YBCO) film. The final diameter of the grains is about 0.1 μm. When highly purified coating solution is used, suppressing the creation of nanocrystallites in the precursor film is an effective way to obtain high-J c YBCO film because the nanocrystallites consist only of CuO. We obtained the highest-J c YBCO film on LaAlO 3 single crystal with a calcining process of 9h43m at 200-250°C. It was 141 nm thick and had a J c of 7.5 MA/cm 2 (77 K, 0 T), as measured by the four-probe method. The firing process of TFA-MOD still has several unsolved problems; why can H 2O and HF gas diffuse quickly within the film? These phenomena can be explained by a model with a quasiliquid consisting of Y, Ba, Cu, O, H, and F. The H 2O and HF can move quickly in the quasiliquid network within the film during the firing process. According to the model, we can get more conversion of CuO nanocrystallites into quasiliquid by increasing the amount of water vapor. J c of the film was increased from 3.3 to 4.5 MA/cm 2 (77 K, 0 T) by increasing the humidity from 4.2% to 12.1% during the long calcining profile of 66h40m at 200-250°C. These results confirm the above model. CuO nanocrystallites in precursor films induce nonstoichiometric metal contents in the quasiliquid. Isolated CuO grains in YBCO film indirectly cause nonstoichiometric quasiliquid in other areas. Such nonstoichiometric quasiliquid leads to non-YBCO materials such as BaO, Y 2O 3, and Y 2Cu 2O 5. Thus, films derived from non-highly purified coating solution and ones prepared with an inappropriate calcining process both have lower J c values. Micrographs obtained by transmission electron microscopy and J c results support this hypothesis.

    本文言語English
    ページ(範囲)3318-3325
    ページ数8
    ジャーナルJournal of Applied Physics
    92
    6
    DOI
    出版ステータスPublished - 2002 9 15

    ASJC Scopus subject areas

    • 物理学および天文学(全般)

    フィンガープリント

    「Growth model and the effect of CuO nanocrystallites on the properties of chemically derived epitaxial thin films of YBa <sub>2</sub>Cu <sub>3</sub>O <sub>7-x</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル