Grain-growth-inhibiting effects of TiC and ZrC precipitates in Fe-0.15-0.30mass%C alloy

Alexandre O. Titov, Ryo Inoue, Hideaki Suito

研究成果: Article査読

10 被引用数 (Scopus)

抄録

The crystallization and precipitation of TiC and ZrC in an Fe-0.05-0.30%C alloy have been studied from the measurement of particles located at interdendritic region and austenite grain boundaries, The particles and γ grains were observed with the samples quenched at 1 673-1 743 K and those for holding at 1 673 K for 0-180 min. In an Fe-0.05-0.30%C-0.03%Ti alloy with soluble oxygen, the precipitation of Ti(O, C)x occurs at 0.15 and 0.30% C, while it does not at 0.05% C. The cross section area of particles increases with increasing carbon contents. In the case of TiC precipitation in an Fe-0.20%C-0.06-0.22%Ti alloy the particles at interdendritic region dissolve and re-precipitate at γ grain boundaries during holding at 1 673 K for 0-120 min. The TiC particles at γ boundaries dissolve after 60 min, whereby resulting in the abnormal grain growth. In the case of ZrC precipitation in an Fe-0.20%C-0.02~0.27%Zr alloy, however, the ZrC particles at interdendritic region dissolve and continuously re-precipitate at γ grain boundaries up to 180 min, whereby resulting in the normal grain growth.

本文言語English
ページ(範囲)301-309
ページ数9
ジャーナルIsij International
48
3
DOI
出版ステータスPublished - 2008
外部発表はい

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Grain-growth-inhibiting effects of TiC and ZrC precipitates in Fe-0.15-0.30mass%C alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル