From ultrafine thiolate-capped copper nanoclusters toward copper sulfide nanodiscs: A thermally activated evolution route

Derrick Mott, Jun Yin, Mark Engelhard, Rameshwori Loukrakpam, Paul Chang, George Miller, In Tae Bae, Narayan Chandra Das, Chongmin Wang, Jin Luo, Chuan Jian Zhong

研究成果: Article査読

70 被引用数 (Scopus)

抄録

This report shows that the size, shape, and composition of presynthesized copper nanoparticles can be nanoengineered through exploiting concurrent interparticle aggregative growth and interfacial carbon-sulfur cleavage in a thermally activated evolution route. This is demonstrated by thermally activated processing of ultrafine copper nanoclusters encapsulated with thiolate monolayer (Cun,(SR)m) toward semiconducting copper sulfide (Cu2S) nanodiscs with controllable sizes and shapes. Under controlled temperatures (120-150 °C), the ultrafine Cun(SR) m nanoclusters, with a size of ∼0.5 nm evidenced by TEM, SAXS-WAXS, DCP-AES, and MALDI-TOF measurements, were shown to evolve into thiolate-capped Cu2S nanodiscs via thermally activated coalescence and copper-catalyzed interfacial C-S cleavage reactivities. The Cu2S nanodiscs, as confirmed by XPS and HRTEM analyses, exhibited controllable and monodispersed sizes depending on the thermal processing parameters, ranging from 5 to 35 nm in the disk dimension and 3-6 nm in the thickness dimension. These nanodiscs are stable and display remarkable 1D/2D ordering upon self-assembly. This process is not a simple digestive ripening of smaller particles because it involves an aggregative nucleation and growth process distinctively different from traditional ripening and a reactive carbon-sulfur bond cleavage controlled by the catalytic effect of copper under the specified temperatures. The coupling of the thermally activated coalescence and C-S bond cleavage to convert the ultrafine Cu nanoclusters toward the formation of Cu2S nanodiscs is highly effective for tuning nanoscale size, shape, and composition, and could find applications in nanoengineering a variety of semiconducting nanocrystals for applications in nanostructured electronic, sensing, and photochemical devices.

本文言語English
ページ(範囲)261-271
ページ数11
ジャーナルChemistry of Materials
22
1
DOI
出版ステータスPublished - 2010 1 12
外部発表はい

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Chemistry

フィンガープリント 「From ultrafine thiolate-capped copper nanoclusters toward copper sulfide nanodiscs: A thermally activated evolution route」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル