Fracture toughness of friction stir welded Invar 36 alloy at low temperature

Yue Zhao, Aiping Wu, Yutaka Sato, Hiroyuki Kokawa

研究成果: Article

2 引用 (Scopus)

抜粋

The fracture toughness of friction stir welded Invar36 alloy, obtained with travelling speed of 2 mm/s and rotational speed from 200 r/min to 1000 r/min, were estimated at low temperature (77 K) by small punch test, and were compared with that at room temperature (298 K) as well. At 298 K, all welds have higher small punch energy than the base material. For the welds acquired with the same welding parameters, the small punch energy tested at 77 K is always higher than the ones at 298 K. The small punch energy of welds trends to increase with decreasing of the rotational speed at both 77 K and 298 K. With rotational speeds equal or less than 400 r/min, the small punch energy of welds is significantly higher than that of the base material at 77 K. The results indicate that the friction stir welds keep excellent ductility at low temperature. With the increase of travelling speed, higher heat input produces a coarser microstructure and leads to the reduction of fracture toughness in the weld.

元の言語English
ページ(範囲)89-92
ページ数4
ジャーナルHanjie Xuebao/Transactions of the China Welding Institution
32
発行部数12
出版物ステータスPublished - 2011 12 1

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Fracture toughness of friction stir welded Invar 36 alloy at low temperature' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用