Fracture resistance of monolithic zirconia molar crowns with reduced thickness

Keisuke Nakamura, Akio Harada, Ryoichi Inagaki, Taro Kanno, Yoshimi Niwano, Percy Milleding, Ulf Örtengren

研究成果: Article査読

99 被引用数 (Scopus)

抄録

Objectives. The purpose of the present study was to analyze the relationship between fracture load of monolithic zirconia crowns and axial/occlusal thickness and to evaluate the fracture resistance of monolithic zirconia crowns with reduced thickness in comparison with that of monolithic lithium disilicate crowns with regular thickness. Materials and methods. Monolithic zirconia crowns (Lava Plus Zirconia, 3M/ESPE) with specified axial/occlusal thicknesses and lithium disilicate crowns (IPS e. max press, Ivoclar/Vivadent) with regular thickness were fabricated using a dental CAD/CAM system and a press technique, respectively. The crowns cemented onto dies were loaded until fracture. Based on measurements of the crown thickness made by micro-CT and the fracture load, multiple regression analysis was performed. Results. It was revealed that the occlusal thickness significantly affected the fracture load (p < 0.01), but the axial thickness did not (p = 0.2828). Although the reduction of the occlusal thickness decreased the fracture resistance of the monolithic zirconia crowns, the fracture load of the zirconia crowns with the occlusal thickness of 0.5 mm (5558 ± 522 N) was significantly higher than that of lithium disilicate crowns with an occlusal thickness of 1.5 mm (3147 ± 409 N). Conclusion. Within the limitations of the present study, it is suggested that monolithic zirconia crown with chamfer width of 0.5 mm and occlusal thickness of 0.5 mm can be used in the molar region in terms of fracture resistance.

本文言語English
ページ(範囲)602-608
ページ数7
ジャーナルActa odontologica Scandinavica
73
8
DOI
出版ステータスPublished - 2015

ASJC Scopus subject areas

  • 歯科学(全般)

フィンガープリント

「Fracture resistance of monolithic zirconia molar crowns with reduced thickness」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル