Formation of 14H long period stacking ordered structure and profuse stacking faults in Mg-Zn-Gd alloys during isothermal aging at high temperature

Michiaki Yamasaki, Minami Sasaki, Masahiko Nishijima, Kenji Hiraga, Yoshihito Kawamura

研究成果: Article査読

403 被引用数 (Scopus)

抄録

This paper proposes a time-temperature-transformation diagram of an Mg-Zn-Gd alloy. An Mg97Zn1Gd2 (at.%) alloy shows different precipitation sequences at low, medium and high temperatures. Low-temperature aging at <523 K brings about coherent β′-phase precipitation to a α-Mg solid solution, resulting in increase in strength of the alloys. However, aging at medium and high temperatures >623 K led to strengthening of the Mg-Zn-Gd alloy, owing to the formation of profuse stacking faults and 14H long period stacking ordered structure from the supersaturated α-Mg matrix, respectively.

本文言語English
ページ(範囲)6798-6805
ページ数8
ジャーナルActa Materialia
55
20
DOI
出版ステータスPublished - 2007 12

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • ポリマーおよびプラスチック
  • 金属および合金

フィンガープリント

「Formation of 14H long period stacking ordered structure and profuse stacking faults in Mg-Zn-Gd alloys during isothermal aging at high temperature」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル