Formation and texture of Bi-2223 phase during sintering in a temperature gradient

X. Y. Lu, A. Nagata, K. Watanabe, T. Nojima, K. Sugawara, S. Hanada, S. Kamada

研究成果: Article査読

6 被引用数 (Scopus)

抄録

The formation and texture of Bi-2223 phase during sintering in a temperature gradient were investigated. Co-precipitated powders with the composition of Bi:Pb:Sr:Ca:Cu=1.85:0.35:1.90:2.05:3.05 were used. Samples set on a silver holder were sintered at 850 °C for 120 h in a vertical tube furnace with a temperature gradient of 15 °C/cm installed in a solenoid-type superconducting magnet. A vertical magnetic field can be applied parallel to the long axis of the furnace. It has been found that the Bi-2223 grains with their c-axis parallel to the axial direction of the vertical tube furnace are formed not only on the surface, but also in the center of the sample sintered at 850 °C for 120 h in 15 °C/cm temperature gradient without magnetic field. Moreover, the sample sintered in the temperature gradient and in a 10 T magnetic field have a stronger c-axis alignment of Bi-2223 phase. It is suggested that both the temperature gradient and magnetic field during sintering are favorable for the c-axis alignment of Bi-2223 phase.

本文言語English
ページ(範囲)602-606
ページ数5
ジャーナルPhysica C: Superconductivity and its applications
412-414
SPEC. ISS.
DOI
出版ステータスPublished - 2004 10

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Formation and texture of Bi-2223 phase during sintering in a temperature gradient」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル