Flux pinning properties at low temperatures in BaHfO3 doped SmBa2Cu3Oy Films

Akihiro Tsuruta, Yutaka Yoshida, Yusuke Ichino, Ataru Ichinose, Kaname Matsumoto, Satoshi Awaji

研究成果: Article

18 引用 (Scopus)


BaHfO3 (BHO) is attracting attention as a new material forming nanorod as well as BaMO3 (BMO: M = \hbox{Zr}, Sn), and it was reported that the flux pinning force of BHO nanorod is effective even at low temperatures. It is essential to understand the flux pinning properties of an APC-doped REBCO film at low temperatures in order to achieve the high-performance superconducting applications. We fabricated 8.4 mol. % BHO-doped SmBa2Cu3Oy (SmBCO) film on LaAlO 3 (LAO) substrates by pulsed laser deposition method and measured the superconducting properties at 77, 65, 40, and 20 K. As for the magnetic field dependence of Jc, the Jc of the BHO-doped SmBCO film was significantly higher than that of the pure SmBCO film at all temperatures. Furthermore, in the magnetic field angular dependence of Jc, the BHO-doped SmBCO film exhibited the peaks of Jc around B//c at 77, 65, and 40 K in 3 T. These results suggested that the flux pinning force of BHO nanorod was effective even at 65 and 40 K.

ジャーナルIEEE Transactions on Applied Superconductivity
出版物ステータスPublished - 2013 2 11

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

フィンガープリント Flux pinning properties at low temperatures in BaHfO<sub>3</sub> doped SmBa<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub> Films' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用